The manufacturer of Powder metallurgy garden tool parts tells you that after the product is put into application, there will be some failures that will occur. This has a certain relationship with the type and quality of the product, but not all of them are caused by quality problems, and may also be caused by improper operation or different operation methods. Summarize some problems that occur during the use of Powder metallurgy garden tool parts manufacturers.

The most common problem in powder metallurgy bearings is tile surface corrosion. Through spectral analysis, it can be found that the concentration of non-ferrous metal elements is high, and more non-ferrous metal costs appear on the element spectrum, or the moisture or acid value in lubricating oil Exceeding the standard will cause this corrosion problem.
The surface of the shaft diameter of the powder metallurgy bearing will also have a certain degree of pull-up and corrosion. The manufacturer of Powder metallurgy garden tool parts tells you that this is also due to the presence of all cutting abrasive particles inside. The abrasive particles are mainly composed of non-ferrous metals. If a certain amount of fretting wear is found on the back of the tile, it may be that the iron concentration is abnormal, and there are more submicron wear particles of iron components.
The manufacturer of Powder metallurgy garden tool parts tells you that through analysis and summary, we can obtain the cause of the failure according to the problem of the powder metallurgy bearing, and formulate an effective correction plan to ensure the effective service life of the product.